PENGARUH KOMPOSISI DAN SUHU PEMBAKARAN TERHADAP SIFAT FISIK, KIMIA, DAN MEKANIK BATA RINGAN BERBAHAN DASAR ABU TERBANG DAN BENTONIT

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:38
Oleh : ANDHY PUSVITA SARI ( NIM :NIM : 10509031 ) Pembimbing : Prof. Dr. Buchari, S1 - Department of Chemistry
Dibuat : 2014, dengan 7 file

Keyword : bata, abu terbang, bentonit, komposisi, suhu

Bata merupakan material konstruksi yang sangat dekat dengan masyarakat.Namun, densitas yang cukup tinggi membuat bata bersifat berat sehingga tenaga, waktu, dan ongkos yang dibutuhkan dalam proyek konstruksi menjadi lebih besar.Pembuatan bata ringan merupakan alternatif untuk masalah tersebut. Abu terbang merupakan limbah dari pembakaran bata. Sifatnya yang ringan dan mudah didapat menjadikan material ini berpotensi menjadi bahan dasar pembuatan bata ringan. Bentonit yang juga mineral lempung digunakan sebagai pengikat abu terbang dalam penelitian ini. Sebanyak sepuluh variasi komposisi abu terbang dan bentonit dibuat dengan perbandingan 90%:10% ; 85%:15% ; 80%:20% ; 75%:25% ; 70%:30% ; 65%:35% ; 60%: 40% ; 55%:45% ; 50%:50%. Sampel bata dicetak dengan ukuran 4cmx4cmx4cm dan dikeringkan selama 7 hari. Selanjutnya, dilakukan pembakaran dengan tiga variasi suhu yaitu 900o C, 1000oC, dan 1000o C selama 2 jam. Penelitian ini dilakukan untuk mempelajari pengaruh terhadap sifat fisik, kimia, serta mekanik yaitu mengukur densitas, persen absorbsi air, ketahanan terhadap asama dan basa, serta kuat tekan. Karakterisasi sampel dilakukan dengan difraksi sinar-X dan SEM (Scanning Electron Microscope). Hasil penelitian menunjukkan bahwa peningkatan suhu dan komposisi abu terbang dapat meningkatkan densitas, menurunkan persentase penyerapan air, ketahanan terhadap asam dan basa semakin baik, dan meningkatkan sifat mekanik sampel bata.

Deskripsi Alternatif :

Bricks are one of a construction material which is very close to the community. However, the density of the common bricks are quite high enough, making the effort, time, and cost required in construction projects become larger. Manufacture of light bricks is one of a great alternative to the problem. Fly ash is a waste material from coal burning. Its light weight and easy to get properties makes this potentially be a raw material for light brick manufactures. Bentonite clay mineral is also used as binder for fly ash in this research. Nine variations of fly ash and bentonite are created : 90%:10% ; 85%:15% ; 80%:20% ; 75%:25% ; 70%:30% ; 65%:35% ; 60%: 40% ; 55%:45% ; 50%:50%. A sample of light brick were printed in the size of 4cm x 4cm x 4cm and dried for 7 days. Furthemore, the burning was done with three variations of temperature : 900o C, 1000oC, and 1100o C for 2 hours. This research was conducted to study the effect of the physical, chemical, and mechanical properties that measure the density, resistance to acidic and alkaline, and mechanical strength. Characterization of sample is carried out by X-ray diffraction and SEM (Scanning Electron Microscopy). The results showed that the increase in the temperature and composition of fly ash could increase the density, decrease the percentage of water absorbtion, resistance to acidic and alkaline is getting better, and improve the mechanical strength of sample brick.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Buchari, Editor: Alice Diniarti

File PDF...