SINTESIS SILIKA NANOPARTIKEL MESOPORI DENGAN MODIFIKASI METODE STOEBER MENGGUNAKAN SURFAKTAN KATIONIK

SYNTHESIS OF MESOPOROUS SILICA NANOPARTICLES BY THE MODIFICATION OF STOEBER METHOD USING CATIONIC SURFACTANT

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:31
Oleh : ALIP FIRMANSAH (NIM : 10508081); Pembimbing 1: Dr. rer. nat. Rino R. Mukti; Pembimbing 2 : Prof. Dr. Ismunandar, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : Mesopori, silika nanopartikel, metode Stoeber, surfaktan kationik

Nanomedicine menggunakan silika nanopartikel mesopori sebagai zat pembawa obat generasi baru karena memiliki luas permukaan yang besar sehingga ideal membawa sejumlah besar agen biogenik. Dalam penelitian ini, material silika nanopartikel mesopori telah dipelajari secara intensif. Nanosilika sebagai pembanding disintesis menggunakan metode Stoeber yang didasarkan pada hidrolisis dan kondensasi tetraetil ortosilikat (TEOS) dengan menggunakan katalis ammonia dalam kondisi basa lemah (pH 9-10). Dari metode Stoeber ini dihasilkan silika nanopartikel dengan ukuran 40-60 nm dengan nilai BET luas permukaan sebesar 477 m2/g. Silika nanopartikel mesopori disintesis dengan memodifikasi metode Stoeber dengan menggunakan surfaktan kationik. Benzalkonium Klorida (sanisol) digunakan sebagai surfaktan kationik yang bertujuan untuk mencegah agregasi dari nanopartikel yang terbentuk sehingga dapat membentuk partikel yang lebih kecil dengan luas permukaan lebih besar disertai adanya pori meso. Nitrogen fisisorpsi menunjukkan hasil BET luas permukaan sebesar 1159 m2/g. Berdasarkan besarnya luas permukaan, diasumsikan bahwa surfaktan kationik Benzalkonium Klorida dapat mengarahkan pembentukan mesopori intrapartikel. Silika nanopartikel Stoeber tidak menunjukkan karakteristik mesopori intrapartikel tetapi menunjukkan pori interpartikel berdasarkan hasil visualisasi dari Scanning Electron Microscopy (SEM).

Deskripsi Alternatif :

Nanomedicine utilizes mesoporous silica nanoparticles to deliver drug because it has large surface area. This properties is ideal to carry large amounts of biogenic agents. In this study, mesoporous silica nanoparticles have been intensively investigated. Nanosilica Stoeber as a controlled material synthesized by Stoeber method that is based on the hydrolysis of tetraethyl orthosilicate (TEOS) using ammonia catalyst under weakly alkaline conditions (pH 9-10). The resulting nanosilica Stoeber has small particle size and large Brunauer-Emmet-Teller (BET) specific surface area of 40-60 nm and 477 m2/g, respectively. The synthesis of mesoporous silica nanoparticle was synthesized by the modification of Stoeber method using cationic surfactant. Benzalkonium Chloride (sanisol) was used as cationic surfactant with purpose to inhibit the aggregation of nanoparticles, hence forming particles with ultralarge surface area, in addition the presence of mesoporosity. Nitrogen physisorption was applied to characterize the product and the results show BET specific surface of 1159 m2/g. Based on this BET value, it is assumed that cationic surfactant Benzalkonium Chloride might lead to the formation of intraparticle mesoporosity. The nanoparticle Stoeber does not show any intrapartcile mesoporore characteristic but showing interparticle mesoporosity as visualized from Scanning Electron Microscopy (SEM).

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing 1: Dr. rer. nat. Rino R. Mukti; Pembimbing 2 : Prof. Dr. Ismunandar, Editor: PKL-SMK

File PDF...