SINTESIS NANOFLUIDA Fe3O4 SEBAGAI KATALIS DALAM PROSES AQUATHERMOLYSIS

Fe3O4 NANOFLUID SYNTHESIS AS CATALYST IN AQUATHERMOLYSIS PROCESS

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:45:07
Oleh : ALFAJRI ASBAHRI (NIM : 10210013); Pembimbing : Dr. Eng. Ferry Iskandar, S1 - Department of Physics
Dibuat : 2014, dengan 7 file

Keyword : Nanofluida Fe3O4, katalis, aquathermolysis, ethylene glycol (EG), X-Ray Diffraction (XRD), Dynamic Light Scattering (DLS)

Nanofluida Fe3O4 sebagai katalis dalam proses aquathermolysis telah berhasil disintesis menggunakan metode dua tahap. Metode dua tahap tersebut terdiri dari


sintesis nanopartikel Fe3O4 menggunakan metode kopresipitasi yang kemudian nanopartikel Fe3O4 yang diperoleh didispersikan kedalam campuran air dan ethylene glycol (EG) dan disonikasi menggunakan ultrasonic bath selama 2 jam. Pada penelitian ini divariasikan penambahan volume air dan EG terhadap based fluid total untuk mengetahui kestabilan nanopartikel Fe3O4 pada nanofluida. Hasil yang diperoleh dikarakterisasi menggunakan X-Ray Diffraction (XRD) dan Dynamic Light Scattering (DLS). Hasil XRD menunjukan bahwa material yang terbentuk merupakan nanopartikel Fe3O4 dengan ukuran kristal 11,8 nm. Kestabilan nanofluida Fe3O4 yang paling baik ketika menggunakan perbandingan air dan EG sebesar 80% : 20% terhadap volume based fluid total dengan distribusi ukuran partikel yang terdispersi adalah sekitar 309 nm. Uji katalitik dilakukan dengan mensimulasikan proses aquathermolysis dalam skala laboraturium dengan mencampurkan minyak berat, air, dan nanofluida Fe3O4 dalam autoclave yang dipanaskan pada temperatur 200 oC selama 6 jam. Hasil yang diperoleh adalah penuruan viskositas minyak berat sebesar 71,3 % lebih baik dibandingkan tanpa


menggunakan katalis yaitu hanya 40,2 %.

Deskripsi Alternatif :

Fe3O4 nanofluids as a catalyst in aquathermolysis process has been successfully synthesized by using a two-step method. The two-step method started with synthesis Fe3O4 nanoparticles using coprecipitation method and then continued by dispersion of the obtained Fe3O4 nanoparticles into a mixture of water and ethylene glycol (EG) with the help of ultrasonic bath for 2 hours. In this study, the


additional volume of water and EG was varied base on the total of based fluid to determine the stability of Fe3O4 nanoparticles in nanofluids. The results obtained were characterized using X-Ray Diffraction (XRD) and Dynamic Light Scattering (DLS). From XRD results showed that Fe3O4 nanoparticles was formed with the crystal size is 11.8 nm. The best stability of Fe3O4 nanofluid obtained when ratio


of water and EG is 80% : 20% on the total of based fluid volume, while the particle size distribution in nanofluids is 309 nm. The catalyst test were carried out in laboratory scale by simulating the aquathermolysis process by mixing


heavy oil, water, and Fe3O4 nanofluids in an autoclave and heated at temperature 200 oC for 6 hours. The result proved that under the use of nanofluids, viscosity of heavy oil decrease up to 71.3%, better than one without catalyst which decrease by only 40.2%.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Eng. Ferry Iskandar, Editor: Alice Diniarti

File PDF...