MEKANIKA MATERIAL HIPERELASTIK : STUDI LITERATUR BERBAGAI PENGUJIAN CHLOROPRENE RUBBER SERTA PENGUJIAN DAN ANALISIS ELASTOMER (KARET INDONESIA) ALAMI NR DAN SINTETIK NBR

HYPERELASTIC MATERIAL MECHANICS : CHLOROPRENE RUBBER TESTING LITERATURE STUDY, EXPERIMENT AND ANALYSIS OF INDONESIAN NATURAL RUBBER NR AND SYNTHETIC RUBBER NBR

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:40:51
Oleh : AGUNG ZENITHYA P.P (NIM :13104011); Pembimbing 1 : Dr. Ir. Bagus Budiwantoro; , Pembimbing 2 : Dr. Ir. Andri Andriyana, S1 - Department of Mechanical Engineering
Dibuat : 2009, dengan 7 file

Keyword : Material Hiperelastik ; Chloroprene Rubber ; Elastomer Alami NR ; Karet Indonesia; Elastomer Sintetik NBR

Elastomer, baik yang merupakan karet alami maupun karet sintetis merupakan salah satu jenis material yang banyak digunakan pada komponen mesin-mesin industri.


Penelitian ini adalah salah satu rantai penelitian mekanika karet yang dilakukan oleh EDC ITB. Namun tugas sarjana ini hanya dibatasi pada pengujian eksperimental beberapa material karet saja. Diharapkan dengan dilakukannya


penelitian ini, dapat diperoleh pengetahuan yang lebih mendalam mengenai sifatsifat mekanik dari elastomer.


Material yang diuji adalah karet alami Indonesia NR (Natural Rubber) karet sintetik Indonesia NBR (Nitrile Butadiene Rubber), dan karet sintetik chloroprene


rubber. Penelitian terhadap karet Indonesia NR dan NBR dilakukan melalui uji tarik sederhana pada tiga tingkat laju regangan yang berbeda (0,001/s; 0,01/s; 0,1/s), sedangkan data hasil pengujian chloroprene Rubber didapat dari literatur yang ditulis oleh Jorgen Bergstorm dalam thesis PHd-nya “Large strain timedependent behavior of elastomeric materials”.


Berdasarkan hasil pengujian dan literatur yang ada, diperoleh kesimpulan bahwa semua spesimen uji adalah bersifat hiperelastik dan viskoelastik. Hal ini dijelaskan dengan terjadinya fenomena-fenomena histerisis, stress softening, dan stress relaxation.

Deskripsi Alternatif :

Both the natural and synthetic elastomers are widely used as the component of indstrial tools and machinary. Because of that reason, it is necessary to improve the knowlede about mechanical caracteristic and behavior of elastomer under certain case of loading.


This research is a part of rubber mechanics research held by EDC ITB. But, this final project only contains the mechanical experiment and analysis of Indonesian Natural Rubber NR Indonesian Synthetic Rubber NBR (Nitrile Butadiene Rubber) and chloroprene rubber.


The uniaxial tension test is subjected to Indonesian rubber specimen using three different strain rates (0,001/s; 0,01/s; 0,1/s), while the experimental result of chloroprene rubber is obtained from a litearture written by Jorgen Bergstorm “Large strain time-dependent behavior of elastomeric materials” Based on the experimental datas and literature, it can be concluded that all of those samples are hiperelastic and viscoelastic due to hysterisis, stress relaxaton and stress softening (time dependent behavior).

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing 1 : Dr. Ir. Bagus Budiwantoro;


    Pembimbing 2 : Dr. Ir. Andri Andriyana, Editor: PKL-SMK

File PDF...