STUDI SINTESIS NANOKRISTAL ZN2SIO4 MENGGUNAKAN METODE SONOKIMIA SEBAGAI SENYAWA INDUK FOTOLUMINESENSI

Undergraduate Theses from JBPTITBPP / 2017-04-21 09:08:46
Oleh : ADREANSYAH (NIM : 10510048), S1 - Department of Chemistry
Dibuat : 2015, dengan 7 file

Keyword : Zn2SiO4, nanokristal, luminesensi, sonokimia

Zn2SiO4 merupakan salah satu jenis material induk luminesensi yang dapat menghasilkan berbagai warna. Pada penelitian ini senyawa Zn2SiO4 disintesis menggunakan
metode sonokimia untuk pertama kali. Reaksi dengan menggunakan gelombang ultrasonik ini dilakukan untuk menghasilkan kristal berukuran nano pada kondisi ruang (25 oC, 1 atm). Reaksi optimum menggunakan sonokimia didapat pada waktu sonikasi, konsentrasi basa, dan waktu aging pembentukan jaringan SiO2 pada 6 jam, 5,38 M, dan 48 jam secara berurutan. Setelah pengeringan pada suhu 100 oC, kristal yang didapat membentuk struktur
willemite yang ditunjukkan oleh bidang hkl pada (003), (401), (521), dan (042) melalui karakterisasi difraksi sinar-X (XRD). Kristal hasil sintesis juga telah diamati melalui mikroskop pindai elektron (SEM). Berdasarkan perhitungan, ukuran kristal hasil sintesis yang didapat sebesar 10,3 nm. Hasil pengukuran energi celah pita kristal melalui refleksi UV-Visual didapat sekitar 3,27 eV. Zn2SiO4 yang disintesis menggunakan metode sonokimia
memiliki sifat yang sebanding dengan metode sintesis lainnya.

Deskripsi Alternatif :

As a luminescence host material, Zn2SiO4 can produce several colors. In this research, Zn2SiO4 has been synthetized by means of sonochemical method for the first time. Through ultrasonic waves, the reaction produced a nano-sized crystal at room condition (25
oC, 1 atm). Sonication time, base concentration, and aging time are 6 hours, 5,38 M, and 48 hours respectively as the optimal condition for the reaction. After drying at 100 oC, the crystal structure was found to be a willemite structure that shown by peaks of at (003), (401), (521), and (042) of hkl reflecting using X-ray diffraction (XRD). The crystal also has been observed by scanning electrone microscope (SEM). By calculating the Full Width of Half Maximum (FWHM), the size of the crystal was found to be 10,3 nm. Meanwhile, the band gap energy was around 3,27 eV obtained from the UV-Visual reflectance spectrum calculation. The sonochemical synthesized Zn2SiO4 has as similar properties as the other crystal by different methods.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Department of Chemistry
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Bambang Prijamboedi, Editor: Alice Diniarti

Download...