KETERURAIAN PLASTIK BIODEGRADABLE PADA KONDISI AEROB SECARA SKALA LABORATORIUM BERDASARKAN ISO 14855-1:2005

DEGRADIBILITY OF PLASTIC BIODEGRADABLE IN LABORATORIUM SCALE ON AEROB CONDITIONS BASED ON ISO 14855-1:2005

Undergraduate Theses from JBPTITBPP / 2018-03-13 15:18:00
Oleh : ACHILLES PETRUS ARDINE HELAHA NIM: 15312027, S1 - Environmental Engineering-FTSL
Dibuat : 2018-03-13, dengan 1 file

Keyword : degradasi, inokulum, kinetika, kontrol kompos, mikroorganisme, plastik biodegradable

Plastik biodegradable merupakan plastik yang dapat terdegradasi oleh mikroorganisme menjadi senyawa sederhana seperti air (H2O), karbon dioksida (CO2), dan biomassa. Plastik biodegradable terbuat dari selulosa dan pati sehingga sangat ramah lingkungan dibandingkan dengan plastik konvensional yang terbuat dari polimer yang sulit terdegradasi. Namun, untuk mendapatkan penilaian yang signifikan mengenai tingkat degradibilitas sampel plastik, hasilnya harus diukur sesuai standar. Penelitian ini menggunakan standar ISO 14855 bagian 1 yang diterbitkan pada tahun 2005 sebagai metode pengujian degradibilitas berdasarkan emisi gas CO2 yang dihasilkan. Sampel uji yang digunakan dalam penelitian ini adalah plastik biodegradable dan kertas saring sebagai kontrol positif. Uji biodegradasi dilakukan pada kondisi pengomposan dengan menggunakan kompos matang dari TPS Sabuga ITB sebagai inokulum. Emisi karbon dioksida yang dihasilkan ditangkap oleh larutan NaOH jenuh dan dievaluasi melalui metode titrasi standar untuk memeriksa hasilnya. Pada penelitian ini, dilakukan peninjauan terhadap karakteristik fisik, kimia dan juga biologi awal dari kompos yang digunakan. Hasil pengujian degradasi plastik biodegradable pada kondisi pengomposan terkontrol selama 60 hari mencapai 22,47±0,017% dan kertas saring mencapai 14,37±0,013%. Penggunaan Standar ISO (International Organization for Standardization) 14855 bagian 1 juga untuk mempelajari dan mengevaluasi kinetika evolusi C-CO2 selama proses biodegradasi material uji menggunakan orde reaksi satu. Hasil penelitian menunjukkan bahwa plastik biodegradable dan kertas tidak menghasilkan karbon yang mudah terhidrolisis (Cr) tetapi menghasilkan tingkat degradasi untuk karbon yang terhidrolisis menengah (Cm) sebesar C-CO2 12,97% dengan nilai k=0,023 hari-1 untuk plastik biodegradable dan 6,69% dengan nilai k=0,005 hari-1 untuk kertas saring, serta karbon yang susah terhidrolisis masing-masing 8,07% dengan nilai k=0,0038 hari-1 untuk plastik biodegradable dan 6,55% dengan nilai k=0,001 hari-1 untuk kertas saring. Tidak terdapat fase lag yang teramati pada pengujian biodegradabilitas plastik biodgradable dan kertas saring sebagai kontrol positif

Deskripsi Alternatif :

Biodegradable plastic is a plastic that can be degraded by microorganisms into simple compounds such as water (H2O) carbon dioxide (CO2), and biomass. Biodegradable plastics are made from focellulose and starch making it very environmentally friendly compared to conventional plastics that hard to degrade. However, to get a significant assessment about biodegradation level of plastic sample, the result should be measured according to standards. This research used ISO 14855 part 1 which was published on 2005 as basic standard. Sample test that used in this research is plastic biodegradable and filter paper as positive control. Biodegradation test was conducted at composting condition using mature compost from TPS Sabuga ITB as inoculum. The result of carbon dioxide emissions were captured by a saturated NaOH solution and evaluated by standard titration method to check the results. In this study, a review of the physical, chemical, and biological characteristics of the compost was used. The degradation results for biodegradable plastic at controlled composting conditions for 60 days reached 22.47 ± 0.017% and filter paper reached 14.37 ± 0.013%. The use of ISO (International Organization for Standardization) 14855 Standard Part 1 is also to study and evaluate the evolutionary kinetics of C-CO2 during the biodegradation process of the test material using first-order reaction. The results showed that biodegradable plastics and filter paper did not produce carbon readily hydrolyzed (Cr) but showing resulted of degradation rates for carbon moderately hydrolyzed (Cm) and carbon slowly hidrolyzed (Cs) from the emision of C-CO2 produced in this study. The resulted of carbon moderately is 12.97% with k=0.023 day-1 for biodegradable plastics and 6.69% with k=0,005 day-1 value for filter paper, and carbon slowly hydrolyzed is 8.07% with k=0.0038 day-1 for biodegradable plastics and 6.55% with k=0.001 day -1 for filter paper. No lag phase was observed in testing biodegradibility of biodegradable plastic and filter paper as a positive control.

Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Environmental Engineering-FTSL
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing I : Dr. Barti Setiani Muntalif

    Pembimbing II : Emenda Sembiring, S.T., M.T., MengSc., Ph.D, Editor: Lili Sawaludin Mulyadi

File PDF...