PABRIKASI MEMBRAN NANOSERAT TIO2/STYROFOAM KOMPOSIT MELALUI METODE ELEKTROSPINNING UNTUK APLIKASI PENJERNIHAN AIR

Undergraduate Theses from JBPTITBPP / 2017-09-27 14:41:01
Oleh : ABDUL RAJAK ( NIM : 20212017 ); Pembimbing : Prof. Dr. Eng. Mikrajuddin Abdullah, S2 - Physics
Dibuat : 2014, dengan 7 file

Keyword : Elektrospinning, multinozzle, multi-syringe, kolektor drum, konveyor kolektor, membran komposit TiO2/Styrofoam, potokatalis, wantex, spektrometer

Pada penelitian ini telah dirancang dua model sistem elektrospinning yaitu sistemmulti-nozzle drum kolektor dan selanjutnya sistem multi-syringe konveyor kolektor. Penelitian ini dibagi menjadi dua tahap, yaitu eksperimen pendahuluan untuk memperoleh data kualitatif dan eksperimen yang kedua untuk memperoleh data kuantitatif.Pada penelitian pendahuluan telah dibuat nanoserat TiO2/Styrofoam komposit dengan menggunakan sistem elektrospinning multinozzle untuk aplikasi






penjernihan air. Membran nanoserat komposit yang dibuat dari larutan prekursor disiapkan dengan melarutkan styrofoam dalam pelarut tetrahydrofuran (THF),






minyak sitronella dan minyak kayu putih. Larutan prekursor yang telah dihasilkan kemudian dicampurkan dengan serbuk TiO2 dengan tiga variasi konsentrasi






(1:15,1:20 dan 1:40). Model limbah air yang digunakan dalam penelitian ini adalah pewarna tekstil wantex dengan konsentrasi 50 ppm. Telah dihasilkan data






kualitatif yang meliputi struktur dan morfologi nanoserat komposit yang dikarakterisasi menggunakan scanning electron microscopy (SEM), energy dispersive x-ray (EDX) dan x-ray difraction (XRD). Aktivitas potokatalis dari membran nanoserat dalam mendegradasi pewarna tekstil wantex telah diamati dibawah sinar matahari selama 4 hari.Penelitian dilanjutkan dengan pabrikasi nanoserat dengan variasi konsentrasi dan






perbandingan yang sama menggunakan sistem elektrospinning multi-syringe konveyor kolektor. Aktivitas potokatalis diamati dibawah lampu pijar 60 watt dalam box uji potokatalis. Pengamatan proses potokatalis telah dilakukan selama 30 jam dan sudah diperoleh hasil pengambilan gambar larutan menggunakan






kamera setiap 6 jam. Data kuantitatif berupa penurunan konsentrasi larutan wantex diambil menggunakan spektrometer sederhana dan spektrometer UV-Vis.






Spektrometer sederhana yang dirancang menggunakan sebuah lampu led dan sensor photodioda yang dapat mengukur karakteristik tegangan keluaran larutan uji. Pengambilan data menggunakan spektrometer sederhana ini dilakukan setiap 2 jam sekali. Sedangkan untuk pengambilan data menggunakan spektrometer Uv-Vis dilakukan setiap 6 jam, data yang diperoleh berupa penurunan absorbansi dari






beberapa larutan setelah perlakuan potokatalis. Hasil data kuantitatif telah menunjukkan bahwa terdapat perbedaan signifikan laju potokatalis antara ketiga






variasi membran. Sejumlah 69% larutan wantex sudah berhasil didegradasi selama 30 jam di bawah sinar lampu pijar tersebut.

Deskripsi Alternatif :

In this research, two models of electrospinning system have been designed, that is multi-nozzle drum collector system and multi-syringe conveyors collector system.






This research is divided into two part, preliminary experiments to obtain the qualitative data and second experiment to obtain the quantitative data.In preliminary research, TiO2/Styrofoam composites nanofiber have been fabricated using an electrospinning multinozzle drum collector system for water purification applications. Composite nanofiber membrane was fabricated from precursor solution prepared by dissolving Styrofoam and TiO2 in the mixture of






tetrahydrofuran (THF), citronella oil and cajuput oil. Then, the precursor solutions is mixed with TiO2 powder with three variations based on concentration(1:15,1:20 and 1:40). The model of wastewater that used in this research is wantex textile dyes with 50 ppm of concentration. The qualitative data have been






obtained that consist of structure and morphology of the membrane that characterized using scanning electron microscopy (SEM), energy dispersive x-ray(EDX) and x-ray difraction (XRD). The photocatalytic activity of composite nanofibers on degradation of wantex textile dyes was investigated under the sun light for 4 days.The research is continued by fabrication nanofiber membrane with the same concentration using an electrospinning multi-syringe conveyor collector system.The photocatalytic activity was investigated under the bulb light with 60 watt of power in the box of photocatalytic test. The observation of photocatalytic process has been carried out for 30 hours and have been obtained a result of taken pictures by camera every 6 hours. Quantitative data of decrease in the concentration of wantex solution has been taken by using a simple spectrometer and UV-Vis






spectrometer. Simple spectrometer that designed is using a LED light and a photodiode sensor which can measure the output voltage characteristics of the test solution. Collecting of quantitative data using a simple spectrometer has been carried out every 2 hours. Whereas, for collecting data using Uv-Vis spectrometer






performed every 6 hours, the data obtained in the form of a decrease the absorbance of the solution after several treatments photocatalytic. Based on the






results of quantitative data, there are significant differences of photocatalytic rate between three variations of membrane. As many as 69% of wantex solution have been successfully degraded for 30 hours under the bulb light.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Eng. Mikrajuddin Abdullah ;






    Dr. Eng. Muhammad Miftahul Munir
    , Editor: Alice Diniarti

File PDF...