STUDI EKSPERIMENTAL MORTAR GEOPOLIMER BERBASIS ABU TERBANG (FLY-ASH) TIPE F (LOW CALCIUM)

EXPERIMENTAL STUDIES OF MORTAR GEOPOLIMER BASED ON LOW CALCIUM FLY ASH (TYPE F)

Master Theses from JBPTITBPP / 2017-09-27 15:23:33
Oleh : ABDI NASSA NAITUTU (NIM : 25006033); Pembimbing : Dr. Ir. Saptahari Sugiri, S2 - Civil Engineering
Dibuat : 2010, dengan 7 file

Keyword : sodium hidroksida, sodium silikat, abu terbang, kuat tekan, kecepatan rambat, porositas.

Salah satu isu lingkungan terbesar yang berkembang saat ini adalah menyangkut perubahan iklim akibat pemanasan global (global warming) yang diakibatkan oleh emisi gas-gas rumah kaca. Diantara gas-gas rumah kaca tersebut, gas karbon dioksida (CO2) memberikan kontribusi sekitar 65% dari total emisi gas karbon dioksida ke atmosfir (McCaffrey, 2002). Dari jumlah tersebut sekitar setengah dari emisi gas karbon dioksida dihasilkan dari proses pembakaran batu kapur sebagai bahan baku utama dalam pembuatan semen, sedangkan setengahnya lagi adalah sebagai akibat dari penggunaan energy atau bahan bakar dalam proses tersebut.


Untuk itu diperlukan upaya-upaya yang menunjang sustainability beton sebagai material konstruksi dengan cara mencari dan mengembangkan material beton yang lebih ramah lingkungan dan rekayasa serta konstruksi beton yang lebih efisien.


Diharapkan dari penelitian mengenai teknologi geopolimer ini dapat mendukung upaya-upaya pengembangan material beton yang lebih ramah lingkungan.


Dari hasil penelitian yang menerapkan dua macam komposisi campuran yang berbeda, diperoleh bahwa komposisi campuran yang memiliki kandungan sodium silika lebih banyak akan mempengaruhi kinerja dari mortar geopolimer. Hal ini dapat dilihat dari hasil kuat tekan yang diperoleh yaitu kuat tekan optimum mencapai 39,43 MPa yang dihasilkan dari komposisi yang menggunakan campuran mix design 2. Besaran kuat tekan rata-rata mortar geopolimer optimum diperoleh dari hasil pengujian dengan melakukan metode perawatan kering permukaan yaitu sebesar 33,12 MPa untuk mix design 1 dan 39,43 MPa pada mix design 2. Hasil pengujian porositas juga menunjukkan nilai yang lebih rendah dibandingkan beton normal, yaitu 9,39% untuk mix design 1 dan 7,67% untuk mix design 2. Kerapatan massa kering dari mix design 1 lebih rendah dibandingkan mix design 2, yaitu 1467,86 kg/m3 untuk mix design 1 dan 1687,14 kg/m3 untuk mix design 2.

Deskripsi Alternatif :

One of the biggest growing environmental issue is concerning change of climate as result of global warming. The global warming is caused by the emission of the greenhouse such as CO2. Among the greenhouse gases, CO2 contributes about 65% of global warming (McCaffrey, 2002), that release to the atmosphere. From the amounts, around half from carbon dioxide gasses emission was combustion from the process of limestone as the main component standard in making cement.


Therefore, it is required efforts supporting suistainability concrete as construction material, by searching dan developing environmental friendly concrete material and construction concrete which more efficient.


Expected from research about this geopolymer technology can support expansion efforts of the development concrete material which is more friendly.


From research result applying two kinds of composition of different mixture, obtained that composition of mixture content more silica sodium will influence performance of mortar geopolymer. Based on research, optimum compressive strength was 39,43 MPa, obtained by using the composition of mix design two. Compressive strength magnitude average of optimum mortar geopolymer obtained from result of examination by doing treatment method of dry surface, that is 33,12 MPa for mix design 1 and 39,43 MPa at mix design 2. Result of the examination of porosity also shows lower value compared to normal concrete, that is 9,39% for mix design 1 and 7,67% for mix design 2. Dry density of mix design 1 is lower than mix design 2, that is 1467,86 kg/m3 for mix design 1 and 1687,14 kg/m3 for mix design 2.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Saptahari Sugiri, Editor: Alice Diniarti

File PDF...